Sepheo sa phekolo ea vulcanization:
Ha vulcanization e sebelisoa e le lisebelisoa tse thibelang likhohlano lihlahisoa tsa metallurgy tsa phofo, li-bearings tse entsoeng ka oli tse entsoeng ka tšepe ke tsona tse sebelisoang haholo.Li-bearings tse kenngoeng ka oli e kentsoeng ka sintered (tse nang le graphite ea 1% -4%) li na le mokhoa o bonolo oa tlhahiso le litšenyehelo tse tlase.Tabeng ea PV<18-25 kg·m/cm 2·sec, e ka nka sebaka sa boronse, alloy ea babbitt le lisebelisoa tse ling tse khahlanong le likhohlano.Leha ho le joalo, tlas'a maemo a boima a ho sebetsa, a kang lebelo le phahameng la ho thella holim'a likhohlano le mojaro o moholo oa li-unit, ho hanyetsa ho apara le bophelo ba likarolo tse sintered li tla fokotseha ka potlako.E le ho ntlafatsa ts'ebetso e khahlanong le khohlano ea likarolo tse khahlanong le likhohlano tse entsoeng ka tšepe, ho fokotsa coefficient ea khohlano, le ho eketsa mocheso oa ho sebetsa ho atolosa mefuta ea eona ea tšebeliso, phekolo ea vulcanization ke mokhoa o lokeloang ke ho phahamisoa.
Sebabole le sulfide tse ngata li na le lintho tse itseng tsa ho tlotsa.Iron sulfide ke setlolo se tiileng se tiileng, haholo-holo tlas'a maemo a omileng a khohlano, boteng ba iron sulfide bo na le khanyetso e ntle ea ho tsietsana.
Lihlahisoa tse entsoeng ka tšepe tse entsoeng ka phofo, tse sebelisang li-capillary pores li ka kenngoa ka bongata ba sebabole.Ka mor'a ho futhumatsa, sebabole le tšepe ka holim'a li-pores li ka hlahisa sulfide ea tšepe, e arolelanoang ka mokhoa o lekanang ho pholletsa le sehlahisoa 'me e bapala lubrication e ntle holim'a ho ferekana 'Me e ka ntlafatsa ts'ebetso ea ho itšeha.Ka mor'a vulcanization, likhohlano le libaka tsa ho itšeha tsa lihlahisoa li boreleli haholo.
Ka mor'a hore tšepe e nang le porous sintered e senyehile, mosebetsi o hlahelletseng ke ho ba le thepa e ntle ea ho ferekanngoa.Ke ntho e khotsofatsang ea ho itlotsa ka tlas'a maemo a ho sebetsa a se nang oli (ke hore, ha ho na oli kapa oli e lumelloang), 'me e na le khanyetso e ntle ea ho ts'oaroa' me e fokotsa ts'ebetso ea ho phunya shaft.Ho phaella moo, litšobotsi tsa likhohlano tsa thepa ena li fapane le lisebelisoa tse tloaelehileng tse khahlanong le likhohlano.Ka kakaretso, ha khatello e khethehileng e ntse e eketseha, coefficient ea likhohlano ha e fetohe haholo.Ha khatello e khethehileng e feta boleng bo itseng, coefficient ea friction e eketseha haholo.Leha ho le joalo, khohlano coefficient ea porous sintered iron ka mor'a kalafo vulcanization ea fokotseha ka ho eketseha ha khatello ea eona e khethehileng mofuteng o moholo oa khatello e khethehileng.Ena ke tšobotsi ea bohlokoa ea thepa e khahlanong le khohlano.
Oli e kenngoeng ka tšepe e entsoeng ka sintered ka mor'a ho senyeha e ka sebetsa hantle ka tlase ho 250 ° C.
Mokhoa oa Vulcanization:
Mokhoa oa phekolo ea vulcanization o batla o le bonolo ebile ha o hloke lisebelisoa tse khethehileng.Mokhoa ona o tjena: kenya sebabole ka har'a crucible 'me ue chese ho qhibiliha.Ha mocheso o laoloa ho 120-130 ℃, metsi a sebabole a molemo nakong ena.Haeba mocheso o phahame haholo, Ha o khone ho kenya letsoho.Sehlahisoa sa sintered se lokelang ho kenngoa se futhumatsoa ho 100-150 ° C, ebe sehlahisoa se qoelisoa ka tharollo ea sebabole e qhibilihisitsoeng ka metsotso e 3-20, 'me sehlahisoa se sa chesang se qoelisoa ka metsotso e 25-30.Ho itšetlehile ka boima ba sehlahisoa, botenya ba lebota le boholo ba ho qoelisoa ho hlokahalang ho fumana nako ea ho qoelisoa.Nako ea ho qoelisoa bakeng sa boima bo tlaase le botenya ba lebota bo fokolang;ka ho fapanyetsana.Ka mor'a leaching, sehlahisoa se ntšoa, 'me sebabole se setseng se tšolloa.Qetellong, kenya sehlahisoa se kentsoeng ka sebōping, se sireletse ka hydrogen kapa mashala, 'me u se chese ho 700-720 ° C bakeng sa 0,5 ho 1 hora.Ka nako ena, sebabole se qoelitsoeng se kopana le tšepe ho hlahisa sulfide ea tšepe.Bakeng sa lihlahisoa tse nang le boima ba 6 ho 6.2 g / cm3, sebabole se ka bang 35 ho 4% (karolo ea boima ba 'mele).Ho futhumatsa le ho besoa ke ho etsa hore sebabole se kene ka har'a masoba a karolo ea tšepe ea sulfide.
Sehlahisoa sa sintered ka mor'a vulcanization se ka phekoloa ka ho qoelisoa ka oli le ho qeta.
Mehlala ea ts'ebeliso ea kalafo ea vulcanization:
1. Li-sleeve tsa li-mill mill shaft Li-sleeve tsa shaft li kenngoa lipheletsong tse peli tsa meqolo e 'meli, kakaretso ea lihlopha tse' nè.Khatello ea moqolo ke lik'hilograma tse 280, 'me lebelo ke 700-1000 rpm (P = 10 kg / cm2, V = 2 m / sec).Sehlahla sa pele sa tin bronze se ne se tlotsoa ka seretse sa oli.Hona joale e nkeloa sebaka ke tšepe ea porous sintered e nang le letsoalo la 5.8 g/cm3 le S content ea 6.8%.Sesebediswa sa pele sa ho tlotsa se ka sebediswa sebakeng sa sesebediswa sa pele sa ho tlotsa.Lahlela marotholi a seng makae feela a oli pele u khanna 'me u sebetse u sa phetse lihora tse 40.Thempereichara ea letsoho e ka ba 40°C feela.;Ho sila 12,000 kg ea phofo, bushing e ntse e sebetsa ka mokhoa o tloaelehileng.
2. Mochini oa li-roller cone ke sesebelisoa sa bohlokoa sa ho cheka oli.Ho na le letsoho le thellang ka holim'a oli ea ho cheka, e tlas'a khatello e kholo (khatello ea P=500 kgf/cm2, lebelo la V=0.15m/sec.), 'me ho na le ho thothomela ho matla le ho thothomela.
Nako ea poso: Jul-12-2021